Ecoblend S65 Black

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

- Industrial grade of PC/ABS alloy

- Material developed for automotive industry

- Grade characterized by good thermal property and good impact

 

Properties Test condition Method Unit Value
Rheological Melt Flow Index 260°C / 5 kg ASTM D1238 g/10min 27
Mechanical Tensile Stress at Yield 50 mm/min. ASTM D638 MPa 50
Mechanical Flexural Maximum Stress 1,3 mm/min ASTM D790 MPa 85
Mechanical Flexural Elastic Modulus 1,3 mm/min ASTM D790 MPa 2600
Mechanical Izod Notched Impact Strength 23°C/3mm ASTM D256 J/m 350
Mechanical Izod Notched Impact Strength -20°C/3mm ASTM D256 J/m 125
Mechanical Rockwell Hardness 23°C ASTM D785 M-scale 115
Mechanical Elongation 50 mm/min ASTM D638 % 30
Thermal Vicat Softening Temperature 49N / 120°C/h ASTM D 1525 °C 122
Thermal Linear Expansion Coefficient 23°C/55°C ISO 11359-2 10^-5 K^-1 8
Flame Behaviour Glow Wire Temperature (G.W.T) S=2.0 mm IEC 695-2-1 °C 650
Flame Behaviour UL 94 Rating S=1.6 mm UL 94 class HB
Flame Behaviour UL 94 Rating S=3.2 mm UL 94 class HB
Electrical Relative Permettivity 1 Mhz – dry IEC 60250 - 2,9
Electrical Dissipation Factor 1 Mhz – dry IEC 60250 - 0,05
Electrical Dielectric Strength S=1 mm IEC 60243-1 KV/mm 25
Electrical Surface Resistivity dry IEC 60093 Ω 10^15
Electrical Volume Resistivity dry IEC 60093 Ω • cm 10^15
Various Density ASTM D792 g/cm³ 1,12
Various Humidity Content at Equilibrium 23°C / 50 % U.R. ISO 62 % 0,2
Various Moulding Shrinkage parallel - % 0,5-0,8