Infino AE-2130

	Properties	Test condition	Method	Unit	Value
Physical	Specific Gravity	Natural or Representative Color	ISO 1183	-	1,23
Physical	Mold Shrinkage (MD)	Flow at 3.2mm(MD)	ISO 2577	%	0.3-0.5
Physical	Mold Shrinkage (TD)	X-Flow at 3.2mm(TD)	ISO 2577	%	0.3-0.5
Physical	ASH Content	-	ISO 3451	%	4
Physical	Melt Flow Index	250°C, 2,16kg	ISO 1133	g/10min	2,8
Physical	Melt Flow Index	260°C , 5kg	ISO 1133	g/10min	21
Mechanical	Tensile Strength at Yield	50mm/min	ISO 527	MPa	58
Mechanical	Tensile Strain at Break	50mm/min	ISO 527	%	90
Mechanical	Tensile Modulus	50mm/min	ISO 527	MPa	2400
Mechanical	Tensile Strength at Break	50mm/min	ISO 527	MPa	55
Mechanical	Flexural Strength	2mm/min	ISO 178	MPa	82
Mechanical	Flexural Modulus	2mm/min	ISO 178	MPa	2500
Mechanical	Izod Impact Strength (notched)	at 23°C, 4mm	ISO 180 1A	KJ/m²	33
Mechanical	Charpy Impact Strength (V-notched)	23°C, 4mm	ISO 179 1eA	KJ/m²	40
Mechanical	Rockwell Hardness	R-scale	ISO 2039-2	-	111
Thermal	Heat Deflection Temperature (unannealed)	1.8 MPa, 4.0mm	ISO 75-2	°C	98
Thermal	Heat Deflection Temperature (unannealed)	0.45 MPa, 4.0mm	ISO 75-2	°C	120
Thermal	Heat Deflection Temperature (annealing)	1.8 MPa, 4.0mm	ISO 75-2	°C	112
Thermal	Heat Deflection Temperature (annealing)	0.45 MPa, 4.0mm	ISO 75-2	°C	125
Thermal	Vicat Softening Temperature	B/50	ISO R 306	°C	132