Non-halogen flame-retardant material with high heat resistance that can be applied to battery charger

Properties Test condition Method Unit Value
Physical Specific Gravity Natural or Representative Color ISO 1183 - 1,18
Physical Melt Flow Index 250°C,10kg ISO 1133 g/10min 19
Mechanical Tensile Strength at Yield 50mm/min ISO 527 MPa 55
Mechanical Tensile Strain at Break 50mm/min ISO 527 % 109
Mechanical Tensile Modulus 50mm/min ISO 527 MPa 2100
Mechanical Tensile Strength at Break 50mm/min ISO 527 MPa 67
Mechanical Flexural Strength 2mm/min ISO 178 MPa 80
Mechanical Flexural Modulus 2mm/min ISO 178 MPa 2100
Mechanical Izod Impact Strength (notched) at 23°C, 4mm ISO 180 1A KJ/m² 65
Mechanical Charpy Impact Strength (V-notched) 23°C, 4mm ISO 179 1eA KJ/m² 70
Mechanical Rockwell Hardness R-scale ISO 2039-2 - 120
Thermal Heat Deflection Temperature (unannealed) 1.8 MPa, 4.0mm ISO 75-2 °C 121
Thermal Heat Deflection Temperature (unannealed) 0.45 MPa, 4.0mm ISO 75-2 °C 135
Thermal Heat Deflection Temperature (annealing) 1.8 MPa, 4.0mm ISO 75-2 °C 123
Thermal Heat Deflection Temperature (annealing) 0.45 MPa, 4.0mm ISO 75-2 °C 135
Thermal Vicat Softening Temperature B/50 ISO R 306 °C 140
Thermal Vicat Softening Temperature B/120 ISO R 306 °C 145
Thermal RTI, Ele 1.5 ,V-0 UL746B °C 130
Thermal RTI, Imp 1.5 ,V-0 UL746B °C 130
Thermal RTI, Str 1.5 ,V-0 UL746B °C 130
Flammability Flammability V-2 UL94 mm 0,75
Flammability Flammability V-0 UL94 mm 1.5,3.0