Niblend S45

PC-ABS easy porcessing alloy, suitable for the injection moulding of pieces with low thick ness

	Properties	Test condition	Method	Unit	Value
Rheological	Melt Flow Index	260°C / 5 kg	ASTM D1238	g/10min	20
Mechanical	Tensile Stress at Yield	50 mm/min.	ASTM D638	MPa	40
Mechanical	Flexural Maximum Stress	1,3 mm/min	ASTM D790	MPa	65
Mechanical	Flexural Elastic Modulus	1,3 mm/min	ASTM D790	MPa	2300
Mechanical	Rockwell Hardness		ASTM D785	R-scale	115
Mechanical	Izod Notched Impact Strength	23°C/3,2 mm	ASTM D256	J/m	400
Mechanical	Izod Notched Impact Strength	-20°C/3,2 mm	ASTM D256	J/m	120
Mechanical	Elongation	50 mm/min	ASTM D638	%	30
Thermal	Vicat Softening Temperature	49N / 120°C/h	ASTM D 1525	°C	115
Thermal	Heat Distortion Temperature H.D.T	1.82 MPa	ASTM D648	°C	106
Thermal	Coef. Dilatazione Termica Lineare	23/55 °C	ISO 11359-2	10^-5 K^-1	8
Flame Behaviour	Glow Wire Temperature (G.W.T)	S=2.0 mm	IEC 695-2-1	°C	650
Flame Behaviour	UL 94 Rating	S=1.6 mm	UL 94	class	HB
Flame Behaviour	UL 94 Rating	S=3.2 mm	UL 94	class	HB
Electrical	Dielectric Strength	S=1 mm	IEC 60243-1	KV/mm	25
Electrical	Relative Permettivity	1 Mhz = secco	IEC 60250	-	2,9
Electrical	Dissipation Factor	1 Mhz = secco	IEC 60250	-	0,05
Electrical	Surface Resistivity	secco	IEC 60093	Ω	10^15
Electrical	Volume Resistivity	secco	IEC 60093	Ω • cm	10^15
Various	Density		ASTM D792	g/cm³	1,1
Various	Humidity Content at Equilibrium	23°C / 50 % U.R.	ISO 62	%	0,2
Various	Moulding Shrinkage	parallel	-	%	0,5-0,8