PC-ABS alloy characterized by good heat resistance, good flow, and easy processing. Grade for injection moulding, particularly indicated for automotive industry.

	Properties	Test condition	Method	Unit	Value
Rheological	Melt Flow Index	260°C / 5 kg	ASTM D1238	g/10min	20
Mechanical	Tensile Stress at Yield	50 mm/min.	ASTM D638	MPa	50
Mechanical	Flexural Maximum Stress	1,3 mm/min	ASTM D790	MPa	80
Mechanical	Flexural Elastic Modulus	1,3 mm/min	ASTM D790	MPa	2300
Mechanical	Rockwell Hardness	23°C	ASTM D785	M-scale	116
Mechanical	Izod Notched Impact Strength	23°C/3mm	ASTM D256	J/m	550
Mechanical	Izod Notched Impact Strength	-20°C/3mm	ASTM D256	J/m	150
Mechanical	Elongation	50 mm/min	ASTM D638	%	>50
Mechanical	Tensile Modulus	50 mm/min	ASTM D638	MPa	2350
Thermal	Vicat Softening Temperature	49N / 120°C/h	ASTM D 1525	°C	123
Thermal	Heat Distortion Temperature H.D.T	1.82 MPa	ASTM D648	°C	110
Thermal	Coef. Dilatazione Termica Lineare	23/55 °C	ISO 11359-2	10^-5 K^-1	8
Thermal	Glow Wire Temperature (G.W.T)	S=2.0 mm	IEC 695-2-12	°C	650
Flame Behaviour	UL 94 Rating	S=1.6 mm	UL 94	class	HB
Flame Behaviour	UL 94 Rating	S=3.2 mm	UL 94	class	HB
Electrical	Dielectric Strength	S=1 mm	IEC 60243-1	KV/mm	25
Electrical	Relative Permettivity	1 Mhz = secco	IEC 60250	-	2,9
Electrical	Dissipation Factor	1 Mhz = secco	IEC 60250	-	0,05
Electrical	Surface Resistivity	secco	IEC 60093	Ω	10^15
Electrical	Volume Resistivity	secco	IEC 60093	Ω • cm	10^15
Various	Density		ASTM D792	g/cm³	1,12
Various	Humidity Content at Equilibrium	23°C / 50 % U.R.	ISO 62	%	0,2
Various	Moulding Shrinkage	parallel	-	%	0,5-0,8