Nipene F20 AGR

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

<font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"> </font></font></font>

Polypropylene homopolymer, reinforced with 20% glass fibre chemically coupled to the polymeric matrix

Properties Test condition Method Unit Value
Rheological Melt Flow Index 230 °C / 2,16 Kg ASTM D1238 g/10min 4,5
Mechanical Tensile Stress at Break 5 mm/min ASTM D638 MPa 80
Mechanical Flexural Maximum Stress 1,3 mm/min ASTM D790 MPa 110
Mechanical Flexural Elastic Modulus 1,3 mm/min ASTM D790 MPa 4500
Mechanical Rockwell Hardness ASTM D785 R-scale 113
Mechanical Izod Notched Impact Strength 23°C/3,2 mm ASTM D256 J/m 110
Mechanical Izod Notched Impact Strength -20°C/3,2 mm ASTM D256 J/m 70
Mechanical Elongation 50 mm/min ASTM D638 % 3,5
Thermal Vicat Softening Temperature 49N / 120°C/h ASTM D 1525 °C 138
Thermal Heat Distortion Temperature H.D.T 1.82 MPa ASTM D648 °C 152
Thermal Linear Expansion Coefficient 23°C/55°C ISO 11359-2 10^-5 K^-1 4
Thermal Glow Wire Temperature (G.W.T) S=2.0 mm IEC 695-2-12 °C 650
Flame Behaviour UL 94 Rating S=1.6 mm UL 94 class HB
Flame Behaviour UL 94 Rating S=3.2 mm UL 94 class HB
Electrical Relative Permettivity 1 Mhz – dry IEC 60250 - 2,7
Electrical Dissipation Factor 1 Mhz – dry IEC 60250 - 0
Electrical Dielectric Strength S=1 mm IEC 60243-1 KV/mm 60
Electrical Surface Resistivity dry IEC 60093 Ω 10^14
Electrical Volume Resistivity dry IEC 60093 Ω • cm 10^15
Various Density ASTM D792 g/cm³ 1,05
Various Humidity Content at Equilibrium 23°C / 50 % U.R. ISO 62 % 0,2
Various Moulding Shrinkage parallel - % 0,3-0,7
Various Moulding Shrinkage transversal - % 0,4-1,0