Niplene F15 AGR

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

Polypropylene homopolymer, reinforced with 15% glass fibre chemically coupled to the polymeric matrix

PropertiesTest conditionMethodUnitValue
RheologicalMelt Flow Index230 °C / 2,16 KgASTM D1238g/10min5
MechanicalTensile Stress at Break5 mm/minASTM D638MPa65
MechanicalFlexural Maximum Stress1,3 mm/minASTM D790MPa95
MechanicalFlexural Elastic Modulus1,3 mm/minASTM D790MPa3500
MechanicalRockwell HardnessASTM D785R-scale112
MechanicalIzod Notched Impact Strength23°C/3,2 mmASTM D256J/m90
MechanicalIzod Notched Impact Strength-20°C/3,2 mmASTM D256J/m60
MechanicalElongation50 mm/minASTM D638%3,5
ThermalVicat Softening Temperature49N / 120°C/hASTM D 1525°C135
ThermalHeat Distortion Temperature H.D.T1.82 MPaASTM D648°C150
ThermalLinear Expansion Coefficient23°C/55°CISO 11359-210^-5 K^-14
Flame BehaviourGlow Wire Temperature (G.W.T)S=2.0 mmIEC 695-2-1°C650
Flame BehaviourUL 94 RatingS=1.6 mmUL 94classHB
Flame BehaviourUL 94 RatingS=3.2 mmUL 94classHB
ElectricalRelative Permettivity1 Mhz – dryIEC 60250-2,7
ElectricalDissipation Factor1 Mhz – dryIEC 60250-0
ElectricalDielectric StrengthS=1 mmIEC 60243-1KV/mm60
ElectricalSurface ResistivitydryIEC 60093Ω10^14
ElectricalVolume ResistivitydryIEC 60093Ω • cm10^15
VariousDensityASTM D792g/cm³1
VariousHumidity Content at Equilibrium23°C / 50 % U.R.ISO 62%0,2
VariousMoulding Shrinkageparallel-%0,4-0,8
VariousMoulding Shrinkagetransversal-%0,5-1,0