Polypropylene homopolymer reinforced with 25% of glass fibre. Standard quality.
Properties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Rheological | Melt Flow Index | 230 °C / 2,16 Kg | ASTM D1238 | g/10min | 1,6 |
Mechanical | Tensile Stress at Break | 5 mm/min | ASTM D638 | MPa | 60 |
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 85 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 4500 |
Mechanical | Izod Notched Impact Strength | 23°C/3mm | ASTM D256 | J/m | 80 |
Mechanical | Izod Notched Impact Strength | -20°C/3mm | ASTM D256 | J/m | 50 |
Mechanical | Rockwell Hardness | ASTM D785 | R-scale | 105 | |
Mechanical | Elongation | 50 mm/min | ASTM D638 | % | 5 |
Thermal | Vicat Softening Temperature | 49N / 120°C/h | ASTM D 1525 | °C | 125 |
Thermal | Heat Distortion Temperature H.D.T | 1.82 MPa | ASTM D648 | °C | 143 |
Thermal | Linear Expansion Coefficient | 23°C/55°C | ISO 11359-2 | 10^-5 K^-1 | 4 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 650 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | HB |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | HB |
Electrical | Relative Permettivity | 1 Mhz – dry | IEC 60250 | - | 2,7 |
Electrical | Dissipation Factor | 1 Mhz – dry | IEC 60250 | - | 0,001 |
Electrical | Dielectric Strength | S=1 mm | IEC 60243-1 | KV/mm | 60 |
Electrical | Surface Resistivity | dry | IEC 60093 | Ω | 10^14 |
Electrical | Volume Resistivity | dry | IEC 60093 | Ω • cm | 10^15 |
Various | Density | ASTM D792 | g/cm³ | 1,08 | |
Various | Humidity Content at Equilibrium | 23°C / 50 % U.R. | ISO 62 | % | 0,2 |
Various | Moulding Shrinkage | parallel | - | % | 0,3-0,8 |
Various | Moulding Shrinkage | transversal | - | % | 0,5-0,8 |