Niplene F40 AGR

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

Polypropylene homopolymer, reinforced with 40% glass fibre chemically coupled to the polymeric matrix

PropertiesTest conditionMethodUnitValue
RheologicalMelt Flow Index230 °C / 2,16 KgASTM D1238g/10min3
MechanicalRockwell HardnessASTM D785R-scale115
MechanicalTensile Modulus5 mm/minISO 527-1/-2MPa9200
MechanicalTensile Stress at Break5 mm/minISO 527-1/-2MPa98
MechanicalElongation5 mm/minISO 527-1/-2%3
MechanicalFlexural Maximum Stress1,3 mm/minISO 178MPa150
MechanicalFlexural Elastic Modulus1,3 mm/minISO 178MPa7600
MechanicalIzod Notched Impact Strength23°CISO 180/AKJ/m²12
MechanicalIzod Notched Impact Strength-20°CISO 180/A-8,5
MechanicalTensile Stress at Break5 mm/minASTM D638MPa105
ThermalLinear Expansion Coefficient23°C/55°CISO 11359-210^-5 K^-13
ThermalVicat Softening Temperature (unannealed)B/50ISO 306°C138
ThermalHeat Distortion Temperature (unannealed)A – 1.80 MPaISO 75A-1/-2°C150
Flame BehaviourGlow Wire Temperature (G.W.T)S=2.0 mmIEC 695-2-1°C650
Flame BehaviourUL 94 RatingS=1.6 mmUL 94classHB
Flame BehaviourUL 94 RatingS=3.2 mmUL 94classHB
ElectricalRelative Permettivity1 Mhz – dryIEC 60250-2,7
ElectricalDissipation Factor1 Mhz – dryIEC 60250-0,001
ElectricalDielectric StrengthS=1 mmIEC 60243-1KV/mm60
ElectricalSurface ResistivitydryIEC 60093Ω10^14
ElectricalVolume ResistivitydryIEC 60093Ω • cm10^15
VariousHumidity Content at Equilibrium23°C / 50 % U.R.ISO 62%0,1
VariousMoulding Shrinkageparallel-%0,15-0,55
VariousMoulding Shrinkagetransversal-%0,25-0,75
VariousDensityISO 1183g/cm³1,22