<font face="Arial"><strong style="COLOR: #0000cc">&nbsp;Polypropylene copolymer reinforced with 45 % of glass fibre, chemically bounded.</strong></font>

<font face="Arial"><strong><span style="COLOR: #0000cc"><i><span style="FONT-SIZE: 10pt; COLOR: red; mso-ansi-language: EN-GB" lang="EN-GB"><font face="Arial"><strong><span style="COLOR: #0000ff">Grade heat stabilized characterized by a good balance </span></strong></font></span></i></span><span style="COLOR: #0000ff"><i><span style="FONT-SIZE: 10pt; COLOR: red; mso-ansi-language: EN-GB" lang="EN-GB"><font face="Arial"><strong style="COLOR: #0000cc">stiffness/impact and good dimensional&nbsp;</strong></font></span></i></span></strong></font>  stability.

Properties Test condition Method Unit Value
Rheological Melt Flow Index 230 °C / 2,16 Kg ASTM D1238 g/10min 3,5
Mechanical Flexural Maximum Stress 1,3 mm/min ASTM D790 MPa 135
Mechanical Flexural Elastic Modulus 1,3 mm/min ASTM D790 MPa 8000
Mechanical Izod Notched Impact Strength 23°C/3mm ASTM D256 J/m 200
Mechanical Rockwell Hardness ASTM D785 R-scale 115
Mechanical Elongation 50 mm/min ASTM D638 % 3,5
Mechanical Tensile Modulus 5 mm/min ASTM D638 MPa 9500
Mechanical Tensile Stress at Break 5 mm/min ASTM D638 MPa 80
Thermal Heat Distortion Temperature H.D.T 1.82 MPa ASTM D648 °C 154
Thermal Linear Expansion Coefficient 23°C/55°C ISO 11359-2 10^-5 K^-1 3
Flame Behaviour Glow Wire Temperature (G.W.T) S=2.0 mm IEC 695-2-1 °C 650
Flame Behaviour UL 94 Rating S=1.6 mm UL 94 class HB
Flame Behaviour UL 94 Rating S=3.2 mm UL 94 class HB
Electrical Relative Permettivity 1 Mhz – dry IEC 60250 - 2,7
Electrical Dissipation Factor 1 Mhz – dry IEC 60250 - 0,001
Electrical Dielectric Strength S=1 mm IEC 60243-1 KV/mm 60
Electrical Surface Resistivity dry IEC 60093 Ω 10^14
Electrical Volume Resistivity dry IEC 60093 Ω • cm 10^15
Various Density ASTM D792 g/cm³ 1,3
Various Humidity Content at Equilibrium 23°C / 50 % U.R. ISO 62 % 0,1
Various Moulding Shrinkage parallel - % 0,2-0,7