Niplene SV30
Produkt anfragen Datenblatt herunterladen Telefonische Beratung +49 40 727702-0
<font size="2" face="Arial-BoldItalicMT" color="#ff0000"><font size="2" face="Arial-BoldItalicMT" color="#ff0000"><font size="2" face="Arial-BoldItalicMT" color="#ff0000"> </font></font></font>
- Polypropylene homopolymer reinforced with 30% of glass beads.
- Grade developed for injection molding of items characterized by good aesthetics and dimensional
stability
Properties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Rheological | Melt Flow Index | 230 °C / 2,16 Kg | ASTM D1238 | g/10min | 12 |
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 37 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 2000 |
Mechanical | Izod Notched Impact Strength | 23°C/3mm | ASTM D256 | J/m | 35 |
Mechanical | Elongation | 5mm/min | ASTM D638 | % | >50 |
Mechanical | Tensile Modulus | 5 mm/min | ASTM D638 | MPa | 2500 |
Mechanical | Tensile Stress at Break | 5 mm/min | ASTM D638 | MPa | 22 |
Thermal | Vicat Softening Temperature | 49N / 120°C/h | ASTM D 1525 | °C | 95 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 650 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | HB |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | HB |
Various | Density | ASTM D792 | g/cm³ | 1,12 | |
Various | Humidity Content at Equilibrium | 23°C / 50 % U.R. | ISO 62 | % | 0,1 |