Niplene T40 HF
Produkt anfragen Datenblatt herunterladen Telefonische Beratung +49 40 727702-0
<font face="Arial"><strong style="COLOR: #0000cc">- Polypropylene homopolymer, filled with 40 % of talcum for injection moulding.</strong></font>
- Grade characterized by high fluidity, good processability high stiffness and good dimensional stabilityProperties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Rheological | Melt Flow Index | 230 °C / 2,16 Kg | ASTM D1238 | g/10min | 22 |
Mechanical | Tensile Stress at Yield | 50 mm/min. | ASTM D638 | MPa | 30 |
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 50 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 4000 |
Mechanical | Izod Notched Impact Strength | 23°C/3mm | ASTM D256 | J/m | 30 |
Mechanical | Rockwell Hardness | ASTM D785 | R-scale | 106 | |
Mechanical | Elongation | 50 mm/min | ASTM D638 | % | 20 |
Thermal | Vicat Softening Temperature | 49N / 120°C/h | ASTM D 1525 | °C | 108 |
Thermal | Heat Distortion Temperature H.D.T | 1.82 MPa | ASTM D648 | °C | 90 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 650 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | HB |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | HB |
Electrical | Relative Permettivity | 1 Mhz – dry | IEC 60250 | - | 2,7 |
Electrical | Dissipation Factor | 1 Mhz – dry | IEC 60250 | - | 0,001 |
Electrical | Dielectric Strength | S=1 mm | IEC 60243-1 | KV/mm | 60 |
Electrical | Surface Resistivity | dry | IEC 60093 | Ω | 10^14 |
Electrical | Volume Resistivity | dry | IEC 60093 | Ω • cm | 10^15 |
Various | Moulding Shrinkage | parallel | - | % | 0,4-0,8 |