Niretan A F15

PA 66 reinforced 15% glass fibre for injection moulding.

	Properties	Test condition	Method	Unit	Value
Mechanical	Tensile Stress at Break	5 mm/min	ASTM D638	MPa	130/90
Mechanical	Flexural Maximum Stress	1,3 mm/min	ASTM D790	MPa	190/110
Mechanical	Flexural Elastic Modulus	1,3 mm/min	ASTM D790	MPa	5500/3500
Mechanical	Izod Notched Impact Strength	23°C/3mm	ASTM D256	J/m	60-80
Mechanical	Rockwell Hardness	23°C	ASTM D785	R-scale	110/90
Thermal	Heat Distortion Temperature H.D.T	1.82 MPa	ASTM D648	°C	240
Thermal	Linear Expansion Coefficient	23°C/55°C	ISO 11359-2	10^-5 K^-1	4
Flame Behaviour	Glow Wire Temperature (G.W.T)	S=2.0 mm	IEC 695-2-1	°C	650
Flame Behaviour	UL 94 Rating	S=1.6 mm	UL 94	class	HB
Flame Behaviour	UL 94 Rating	S=3.2 mm	UL 94	class	HB
Electrical	Surface Resistivity	dry	IEC 60093	Ω	10^14/10^13
Electrical	Volume Resistivity	dry	IEC 60093	Ω • cm	10^15/10^12
Various	Moulding Shrinkage	parallel	-	%	0,7/1,2
Physical	Density	23°C	ASTM D792	g/cm³	1,24
Physical	Water Absorption	24h - 23°C	ASTM D570	%	8
Physical	Humidity Absorption from Atmosphere	23°C – 50% HR	ASTM D570	%	2,4
Physical	Cristalline Melting Temperature	DSC	-	°C	260