Niretan A F30 AE/V0

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

Polyamide 66 reinforced with 30% of glass fibre, flame retarded. U.L. 94 rating: V0 at 1,6 mm

PropertiesTest conditionMethodUnitValue
MechanicalTensile Stress at Yield50 mm/min.ASTM D638MPa130/80
MechanicalFlexural Maximum Stress1,3 mm/minASTM D790MPa160/110
MechanicalFlexural Elastic Modulus1,3 mm/minASTM D790MPa9500/6000
MechanicalIzod Notched Impact Strength23°C/3mmASTM D256J/m70/90
MechanicalIzod Notched Impact Strength-20°C/3mmASTM D256J/m50/70
MechanicalRockwell HardnessASTM D785R-scale115/90
ThermalHeat Distortion Temperature H.D.T1.82 MPaASTM D648°C245
ThermalLinear Expansion Coefficient23°C/55°CISO 11359-210^-5 K^-14
Flame BehaviourGlow Wire Temperature (G.W.T)S=2.0 mmIEC 695-2-1°C960
Flame BehaviourUL 94 RatingS=1.6 mmUL 94classV0
Flame BehaviourUL 94 RatingS=3.2 mmUL 94classV0
ElectricalRelative Permettivity1 Mhz – dryIEC 60250-3,5/4,0
ElectricalDissipation Factor1 Mhz – dryIEC 60250-0,02/0,1
ElectricalDielectric StrengthS=1 mmIEC 60243-1KV/mm30/35
ElectricalSurface ResistivitydryIEC 60093Ω10^14/10^13
ElectricalVolume ResistivitydryIEC 60093Ω • cm10^15/10^12
VariousMoulding Shrinkageparallel-%0,3-0,7
PhysicalDensity23°CASTM D792g/cm³1,56
PhysicalWater Absorption24h - 23°CASTM D570%6
PhysicalHumidity Absorption from Atmosphere23°C – 50% HRASTM D570%2
PhysicalCristalline Melting TemperatureDSC-°C260