<font face="Arial"><strong>Polyamide 66 reinforced with 30% of glass fibre, for injection moulding.</strong></font>

Material stabilized, high heat ageing resistance.
Properties Test condition Method Unit Value
Mechanical Flexural Maximum Stress 1,3 mm/min ASTM D790 MPa 270/200
Mechanical Flexural Elastic Modulus 1,3 mm/min ASTM D790 MPa 8600/6500
Mechanical Izod Notched Impact Strength 23°C/3mm ASTM D256 J/m 120/150
Mechanical Izod Notched Impact Strength -20°C/3mm ASTM D256 J/m 60/90
Mechanical Elongation 5mm/min ASTM D638 % 3/5
Mechanical Tensile Modulus 5 mm/min ASTM D638 MPa 9500/7000
Mechanical Tensile Stress at Break 5 mm/min ASTM D638 MPa 170/110
Thermal Heat Distortion Temperature H.D.T 1.82 MPa ASTM D648 °C 245
Thermal Linear Expansion Coefficient 23°C/55°C ISO 11359-2 10^-5 K^-1 3
Flame Behaviour Glow Wire Temperature (G.W.T) S=2.0 mm IEC 695-2-1 °C 650
Flame Behaviour UL 94 Rating S=1.6 mm UL 94 class HB
Flame Behaviour UL 94 Rating S=3.2 mm UL 94 class HB
Electrical Relative Permettivity 1 Mhz – dry IEC 60250 - 3,5/4,0
Electrical Dissipation Factor 1 Mhz – dry IEC 60250 - 0,02/0,1
Electrical Dielectric Strength S=1 mm IEC 60243-1 KV/mm 30/35
Electrical Surface Resistivity dry IEC 60093 Ω 10^14/10^13
Electrical Volume Resistivity dry IEC 60093 Ω • cm 10^15/10^12
Various Moulding Shrinkage parallel - % 0,3-0,7
Physical Density 23°C ASTM D792 g/cm³ 1,36
Physical Water Absorption 24h - 23°C ASTM D570 % 5,5
Physical Humidity Absorption from Atmosphere 23°C – 50% HR ASTM D570 % 1,8
Physical Cristalline Melting Temperature DSC - °C 260