Niretan A F50
Produkt anfragen Datenblatt herunterladen Telefonische Beratung +49 40 727702-0
<font size="2" face="Arial-BoldMT" color="#ff0000"><font size="2" face="Arial-BoldMT" color="#ff0000"><font size="2" face="Arial-BoldMT" color="#ff0000"> </font></font></font>
Polyamide 66, reinforced with 50% of glass fibre, for injection moulding of parts that needs
maximal stiffness and dimensional stability.
Properties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Mechanical | Tensile Stress at Break | 5 mm/min | ASTM D638 | MPa | 210/120 |
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 340/240 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 14000/10000 |
Mechanical | Izod Notched Impact Strength | 23°C/3mm | ASTM D256 | J/m | 150/200 |
Mechanical | Izod Notched Impact Strength | -20°C/3mm | ASTM D256 | J/m | 90/130 |
Mechanical | Rockwell Hardness | ASTM D785 | R-scale | 118/90 | |
Mechanical | Elongation | 50 mm/min | ASTM D638 | % | 2,0/3,5 |
Thermal | Heat Distortion Temperature H.D.T | 1.82 MPa | ASTM D648 | °C | 250 |
Thermal | Linear Expansion Coefficient | 23°C/55°C | ISO 11359-2 | 10^-5 K^-1 | 2,2 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 650 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | HB |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | HB |
Electrical | Relative Permettivity | 1 Mhz – dry | IEC 60250 | - | 3,5/4,0 |
Electrical | Dissipation Factor | 1 Mhz – dry | IEC 60250 | - | 0,02/0,1 |
Electrical | Dielectric Strength | S=1 mm | IEC 60243-1 | KV/mm | 30/35 |
Electrical | Surface Resistivity | dry | IEC 60093 | Ω | 10^14/10^13 |
Electrical | Volume Resistivity | dry | IEC 60093 | Ω • cm | 10^15/10^12 |
Various | Moulding Shrinkage | parallel | - | % | 0,2-0,5 |
Physical | Density | 23°C | ASTM D792 | g/cm³ | 1,56 |
Physical | Water Absorption | 24h - 23°C | ASTM D570 | % | 6 |
Physical | Humidity Absorption from Atmosphere | 23°C – 50% HR | ASTM D570 | % | 2 |
Physical | Cristalline Melting Temperature | DSC | - | °C | 260 |