Niretan A SV30

Polyamide 66 filled with 30% of glass beads for injection moulding.

Grade with good dimensional stability and isotropic properties.

	Properties	Test condition	Method	Unit	Value
Physical	Density	23°C	ASTM D792	g/cm³	1.36
Physical	Water Absorption	24h - 23°C	ASTM D570	%	5.5
Physical	Humidity Absorption from Atmosphere	23°C – 50% HR	ASTM D570	%	1.8
Physical	Cristalline Melting Temperature	DSC	-	°C	260
Mechanical	Tensile Modulus	50 mm/min	ASTM D638	MPa	4400/2300
Mechanical	Tensile Stress at Break	5 mm/min	ASTM D638	MPa	60/35
Mechanical	Elongation	50 mm/min	ASTM D638	%	8/20
Mechanical	Flexural Maximum Stress	1,3 mm/min	ASTM D790	MPa	95/55
Mechanical	Flexural Elastic Modulus	1,3 mm/min	ASTM D790	MPa	4200/2250
Mechanical	Izod Notched Impact Strength	23°C/3mm	ASTM D256	J/m	70/110
Mechanical	Izod Notched Impact Strength	0°C/3mm	ASTM D256	J/m	-
Mechanical	Rockwell Hardness		ASTM D785	R-scale	110/80
Mechanical	Izod Notched Impact Strength	-20°C/3,2 mm	ASTM D256	J/m	-
Thermal	Vicat Softening Temperature	49N / 120°C/h	ASTM D 1525	°C	225
Thermal	Linear Expansion Coefficient	23°C/55°C	ISO 11359-2	10^-5 K^-1	6
Flame Behaviour	Glow Wire Temperature (G.W.T)	S=2.0 mm	IEC 695-2-1	°C	650
Flame Behaviour	UL 94 Rating	S=1.6 mm	UL 94	class	HB
Flame Behaviour	UL 94 Rating	S=3.2 mm	UL 94	class	HB
Electrical	Relative Permettivity	1 Mhz – dry	IEC 60250	-	3.5/4.0
Electrical	Dissipation Factor	1 Mhz – dry	IEC 60250	-	0.02/0.1
Electrical	Dielectric Strength	S=1 mm	IEC 60243-1	KV/mm	30/25
Electrical	Surface Resistivity	dry	IEC 60093	Ω	10^14 / 10^13
Electrical	Volume Resistivity	dry	IEC 60093	Ω • cm	10^15 / 10^12
Various	Moulding Shrinkage	parallel	-	%	0.6 -1.2
Various	Moulding Shrinkage	transversal	-	%	-