Polyamide 66 reinforced with 30% of Talcum, for injection moulding.
Properties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 105 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 5400 |
Mechanical | Izod Notched Impact Strength | 23°C/3mm | ASTM D256 | J/m | 50 |
Mechanical | Elongation | 5mm/min | ASTM D638 | % | 5 |
Mechanical | Tensile Modulus | 5 mm/min | ASTM D638 | MPa | 6200 |
Mechanical | Tensile Stress at Break | 5 mm/min | ASTM D638 | MPa | 60 |
Thermal | Vicat Softening Temperature | 49N / 120°C/h | ASTM D 1525 | °C | 210 |
Thermal | Heat Distortion Temperature H.D.T | 1.82 MPa | ASTM D648 | °C | 80 |
Thermal | Linear Expansion Coefficient | 23°C/55°C | ISO 11359-2 | 10^-5 K^-1 | 6 |
Thermal | Heat Distortion Temperature H.D.T | 0,455 MPa | ASTM D648 | °C | 220 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 650 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | HB |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | HB |
Various | Moulding Shrinkage | parallel | - | % | 0,7-1,2 |
Physical | Density | 23°C | ASTM D792 | g/cm³ | 1,36 |
Physical | Water Absorption | 24h - 23°C | ASTM D570 | % | 5 |
Physical | Humidity Absorption from Atmosphere | 23°C – 50% HR | ASTM D570 | % | 2 |
Physical | Cristalline Melting Temperature | DSC | - | °C | 260 |