Niretan B 27 M

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

Polyamide 6 impact modified, easy flowing, for injection moulding.

PropertiesTest conditionMethodUnitValue
MechanicalTensile Stress at Yield50 mm/min.ASTM D638MPa65/40
MechanicalFlexural Maximum Stress1,3 mm/minASTM D790MPa80-40
MechanicalFlexural Elastic Modulus1,3 mm/minASTM D790MPa2700/900
MechanicalRockwell Hardness23°CASTM D785R-scale100/85
MechanicalIzod Notched Impact Strength23°C/3,2 mmASTM D256J/m130/280
MechanicalIzod Notched Impact Strength-20°C/3,2 mmASTM D256J/m110/180
MechanicalElongation50 mm/minASTM D638%50/200
ThermalHeat Distortion Temperature H.D.T1.82 MPaASTM D648°C50
ThermalLinear Expansion Coefficient23°C/55°CISO 11359-210^-5 K^-110
Flame BehaviourGlow Wire Temperature (G.W.T)S=2.0 mmIEC 695-2-1°C650
Flame BehaviourUL 94 RatingS=1.6 mmUL 94classHB
Flame BehaviourUL 94 RatingS=3.2 mmUL 94classHB
ElectricalDielectric StrengthS=1 mmIEC 60243-1KV/mm30/25
ElectricalRelative Permettivity1 Mhz – dryIEC 60250-3,5/4,0
ElectricalDissipation Factor1 Mhz – dryIEC 60250-0,02/0,1
ElectricalSurface ResistivitydryIEC 60093Ω10^14/10^13
ElectricalVolume ResistivitydryIEC 60093Ω • cm10^15/10^12
VariousMoulding Shrinkageparallel-%1,0-2,5
PhysicalDensity23°CASTM D792g/cm³1,10
PhysicalHumidity Absorption from Atmosphere23°C – 50% HRASTM D570%2,5
PhysicalCristalline Melting TemperatureDSC-°C220