Niretan B AE/V0
Produkt anfragen Datenblatt herunterladen Telefonische Beratung +49 40 727702-0
<font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"> </font></font></font>
Polyamide 6 flame retardant as per UL 94 V0 at 1.6 mm rating
Properties | Test condition | Method | Unit | Value | |
---|---|---|---|---|---|
Mechanical | Flexural Maximum Stress | 1,3 mm/min | ASTM D790 | MPa | 120/60 |
Mechanical | Flexural Elastic Modulus | 1,3 mm/min | ASTM D790 | MPa | 2800/800 |
Mechanical | Rockwell Hardness | ASTM D785 | R-scale | 120/102 | |
Mechanical | Izod Notched Impact Strength | 23°C/3,2 mm | ASTM D256 | J/m | 50/600 |
Mechanical | Izod Notched Impact Strength | -20°C/3mm | ASTM D256 | J/m | 45/500 |
Mechanical | Elongation | 5mm/min | ASTM D638 | % | >60/>200 |
Mechanical | Tensile Stress at Break | 5 mm/min | ASTM D638 | MPa | 60/30 |
Mechanical | Tensile Stress at Yield | 5 mm/min | ASTM D638 | MPa | 80/40 |
Thermal | Heat Distortion Temperature H.D.T | 1.82 MPa | ASTM D648 | °C | 70 |
Thermal | Linear Expansion Coefficient | 23°C/55°C | ISO 11359-2 | 10^-5 K^-1 | 7,5 |
Flame Behaviour | Glow Wire Temperature (G.W.T) | S=2.0 mm | IEC 695-2-1 | °C | 960 |
Flame Behaviour | UL 94 Rating | S=1.6 mm | UL 94 | class | V0 |
Flame Behaviour | UL 94 Rating | S=3.2 mm | UL 94 | class | V0 |
Electrical | Dielectric Strength | S=1 mm | IEC 60243-1 | KV/mm | 60/40 |
Electrical | Relative Permettivity | 1 Mhz = secco | IEC 60250 | - | 3,8 |
Electrical | Dissipation Factor | 1 Mhz = secco | IEC 60250 | - | 0,03 |
Electrical | Surface Resistivity | secco | IEC 60093 | Ω | 10^12/10^10 |
Electrical | Volume Resistivity | secco | IEC 60093 | Ω • cm | 10^15/10^11 |
Physical | Density | 23°C | ASTM D792 | g/cm³ | 1,16 |
Physical | Water Absorption | 24h - 23°C | ASTM D570 | % | 9/10 |
Physical | Humidity Absorption from Atmosphere | 23°C – 50% HR | ASTM D570 | % | 25/3,4 |
Physical | Cristalline Melting Temperature | DSC | - | °C | 215/220 |