Niretan B F30 AE/V0

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

<font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"><font size="1" face="Verdana-Italic" color="#ff0000"> </font></font></font>

Polyamide 6 reinforced with 30% glass fibre; flame retardant as per UL 94 V0 at 1.6 mm rating

Properties Test condition Method Unit Value
Mechanical Flexural Maximum Stress 1,3 mm/min ASTM D790 MPa 180/120
Mechanical Flexural Elastic Modulus 1,3 mm/min ASTM D790 MPa 8500/600
Mechanical Rockwell Hardness ASTM D785 R-scale 115
Mechanical Izod Notched Impact Strength 23°C/3,2 mm ASTM D256 J/m 90/140
Mechanical Izod Notched Impact Strength -20°C/3,2 mm ASTM D256 J/m 70/120
Mechanical Elongation 5mm/min ASTM D638 % 2,0/4,0
Mechanical Tensile Stress at Break 5 mm/min ASTM D638 MPa 140/100
Thermal Heat Distortion Temperature H.D.T 1.82 MPa ASTM D648 °C 205
Thermal Linear Expansion Coefficient 23°C/55°C ISO 11359-2 10^-5 K^-1 4
Flame Behaviour Glow Wire Temperature (G.W.T) S=2.0 mm IEC 695-2-1 °C 960
Flame Behaviour UL 94 Rating S=1.6 mm UL 94 class V0
Flame Behaviour UL 94 Rating S=3.2 mm UL 94 class V0
Electrical Dielectric Strength S=1 mm IEC 60243-1 KV/mm 34/24
Electrical Relative Permettivity 1 Mhz = secco IEC 60250 - 3,8/4,2
Electrical Dissipation Factor 1 Mhz = secco IEC 60250 - 0,02/0,12
Electrical Surface Resistivity secco IEC 60093 Ω 10^14/10^13
Electrical Volume Resistivity secco IEC 60093 Ω • cm 10^15/10^12
Various Moulding Shrinkage parallel - % 0,3-0,6
Physical Density 23°C ASTM D792 g/cm³ 1,55
Physical Water Absorption 24h - 23°C ASTM D570 % 6
Physical Humidity Absorption from Atmosphere 23°C – 50% HR ASTM D570 % 2
Physical Cristalline Melting Temperature DSC - °C 220