Niretan B SV30

Produkt anfragen   Datenblatt herunterladen    Telefonische Beratung +49 40 727702-0

 

Polyamide 6 filled with 30 % of glass spheres, for injection moulding of parts that needs rigidity, dimensional stability and isotropic properties.

PropertiesTest conditionMethodUnitValue
MechanicalTensile Stress at Yield50 mm/min.ASTM D638MPa75-45
MechanicalTensile Stress at Break5 mm/minASTM D638MPa75-45
MechanicalFlexural Maximum Stress1,3 mm/minASTM D790MPa100
MechanicalFlexural Elastic Modulus1,3 mm/minASTM D790MPa4500-1500
MechanicalIzod Notched Impact Strength23°C/3mmASTM D256J/m70-100
MechanicalIzod Notched Impact Strength-20°C/3mmASTM D256J/m50-60
MechanicalRockwell Hardness23°CASTM D785R-scale110-80
MechanicalElongation50 mm/minASTM D638%3-10
ThermalHeat Distortion Temperature H.D.T1.82 MPaASTM D648°C120
ThermalLinear Expansion Coefficient23°C/55°CISO 11359-210^-5 K^-16
Flame BehaviourGlow Wire Temperature (G.W.T)S=2.0 mmIEC 695-2-1°C650
Flame BehaviourUL 94 RatingS=1.6 mmUL 94classHB
Flame BehaviourUL 94 RatingS=3.2 mmUL 94classHB
ElectricalRelative Permettivity1 Mhz – dryIEC 60250-3,5/4,0
ElectricalDissipation Factor1 Mhz – dryIEC 60250-0,02/0,1
ElectricalDielectric StrengthS=1 mmIEC 60243-1KV/mm30/25
ElectricalSurface ResistivitydryIEC 60093Ω10^14/10^13
ElectricalVolume ResistivitydryIEC 60093Ω • cm10^15/10^12
VariousMoulding Shrinkageparallel-%0,5-1,2
PhysicalDensity23°CASTM D792g/cm³1,32
PhysicalWater Absorption24h - 23°CASTM D570%6
PhysicalHumidity Absorption from Atmosphere23°C – 50% HRASTM D570%2,4
PhysicalCristalline Melting TemperatureDSC-°C220