Material with superior chemical resistance that can be applied to the interior/exterior material of house hold appliances that require he at resistance
| Properties | Test condition | Method | Unit | Value | |
|---|---|---|---|---|---|
| Thermal | Vicat Softening Temperature | B/50 | ISO R 306 | °C | 104 |
| Thermal | Heat Deflection Temperature (annealing) | 0.45 MPa, 4.0mm | ISO 75-2 | °C | 101 |
| Thermal | Heat Deflection Temperature (annealing) | 1.8 MPa, 4.0mm | ISO 75-2 | °C | 92 |
| Thermal | Heat Deflection Temperature (unannealed) | 0.45 MPa, 4.0mm | ISO 75-2 | °C | 94 |
| Thermal | Heat Deflection Temperature (unannealed) | 1.8 MPa, 4.0mm | ISO 75-2 | °C | 78 |
| Mechanical | Rockwell Hardness | R-scale | ISO 2039-2 | - | 106 |
| Mechanical | Charpy Impact Strength (V-notched) | 23°C, 4mm | ISO 179 1eA | KJ/m² | 28 |
| Mechanical | Izod Impact Strength (notched) | at 23°C, 4mm | ISO 180 1A | KJ/m² | 34 |
| Mechanical | Flexural Modulus | 2mm/min | ISO 178 | MPa | 2100 |
| Mechanical | Flexural Strength | 2mm/min | ISO 178 | MPa | 65 |
| Mechanical | Tensile Strength at Break | 50mm/min | ISO 527 | MPa | 30 |
| Mechanical | Tensile Modulus | 50mm/min | ISO 527 | MPa | 2000 |
| Mechanical | Tensile Strain at Break | 50mm/min | ISO 527 | % | 19 |
| Mechanical | Tensile Strength at Yield | 50mm/min | ISO 527 | MPa | 44 |
| Physical | Melt Flow Index | 250°C,10kg | ISO 1133 | g/10min | 16 |
| Physical | Specific Gravity | Natural or Representative Color | ISO 1183 | - | 1,1 |