Starex VH-0819

Flame -r tardant ABS material with the characte ristic of high flow that can be used for the exterior material of large TV and OA devices

	Properties	Test condition	Method	Unit	Value
Flammability	Flammability	5VB	UL94	mm	3
Flammability	Flammability	V-0	UL94	mm	2.1-2.3, 3.0
Thermal	Vicat Softening Temperature	B/120	ISO R 306	°C	87
Thermal	Vicat Softening Temperature	B/50	ISO R 306	°C	85
Thermal	Heat Deflection Temperature (unannealed)	0.45 MPa, 4.0mm	ISO 75-2	°C	79
Thermal	Heat Deflection Temperature (unannealed)	1.8 MPa, 4.0mm	ISO 75-2	°C	70
Mechanical	Rockwell Hardness	R-scale	ISO 2039-2	-	105
Mechanical	Charpy Impact Strength (V-notched)	23°C, 4mm	ISO 179 1eA	KJ/m²	25
Mechanical	Izod Impact Strength (notched)	at 23°C, 4mm	ISO 180 1A	KJ/m²	22
Mechanical	Flexural Modulus	2mm/min	ISO 178	MPa	2300
Mechanical	Flexural Strength	2mm/min	ISO 178	MPa	67
Mechanical	Tensile Strength at Break	50mm/min	ISO 527	MPa	32
Mechanical	Tensile Modulus	50mm/min	ISO 527	MPa	2200
Mechanical	Tensile Strain at Break	50mm/min	ISO 527	%	10
Mechanical	Tensile Strength at Yield	50mm/min	ISO 527	MPa	42
Physical	Melt Flow Index	200°C, 5kg	ISO 1133	g/10min	8
Physical	Specific Gravity	Natural or Representative Color	ISO 1183	-	1,16