Starex WR-9300HF
Produkt anfragen Datenblatt herunterladen Telefonische Beratung +49 40 727702-0
| Properties | Test condition | Method | Unit | Value | |
|---|---|---|---|---|---|
| Appearance | Yellowness Index | 3,2mm | ASTM D1925 | - | 25 |
| Flammability | Flammability | HB | UL94 | mm | 1,5 |
| Thermal | Vicat Softening Temperature | B/50 | ISO R 306 | °C | 100 |
| Thermal | Heat Deflection Temperature (unannealed) | 1.8 MPa, 4.0mm | ISO 75-2 | °C | 80 |
| Mechanical | Tensile Strength at Yield | 5mm/min | ISO 527 | MPa | 44 |
| Mechanical | Izod Impact Strength (notched) | -30°C, 4mm | ISO 180 1A | KJ/m² | 5,4 |
| Mechanical | Rockwell Hardness | R-scale | ISO 2039-2 | - | 106 |
| Mechanical | Charpy Impact Strength (V-notched) | 23°C, 4mm | ISO 179 1eA | KJ/m² | 14 |
| Mechanical | Izod Impact Strength (notched) | at 23°C, 4mm | ISO 180 1A | KJ/m² | 12,1 |
| Mechanical | Flexural Modulus | 2mm/min | ISO 178 | MPa | 2100 |
| Mechanical | Flexural Strength | 2mm/min | ISO 178 | MPa | 67 |
| Physical | Melt Flow Index | 250°C, 2,16kg | ISO 1133 | g/10min | 6,5 |
| Physical | Mold Shrinkage (TD) | X-Flow at 3.2mm(TD) | ISO 2577 | % | 0,26 |
| Physical | Mold Shrinkage (MD) | Flow at 3.2mm(MD) | ISO 2577 | % | 0,22 |
| Physical | Melt Flow Index | 220°C, 10kg | ISO 1133 | g/10min | 12 |
| Physical | Specific Gravity | Natural or Representative Color | ISO 1183 | - | 1,07 |